Abrasion-resistant plastic articles

ABSTRACT

An abrasion-resistant article and method for making is disclosed. The article includes a plastic substrate and a gradational coating applied by plasma-enhanced chemical vapor deposition to the surface thereof.

This application is a division of application Ser. No. 336,277, filedApr. 11, 1989, now U.S. Pat. No. 4,927,704.

BACKGROUND OF THE INVENTION

This invention relates generally to plastic articles, and moreparticularly to polycarbonate articles exhibiting improved abrasionresistance, together with improved resistance to cracking under exposureto thermal and mechanical stresses.

Engineering resins are well-known, commercially available materialspossessing physical and chemical properties which are useful in a widevariety of applications. For example, polycarbonates, because of theirexcellent breakage resistance, have replaced glass in many products,such as automobile headlamps and stoplight lenses; safety shields inwindows, architectural glazing, and the like. However, major defectsexhibited by polycarbonates are their very low scratch-resistance andtheir susceptibility to ultraviolet light-induced degradation.

Methods for improving the scratch-resistance of plastics such aspolycarbonate have involved disposing an inorganic protective layer onthe surface of the polycarbonate. For example, in Kaganowicz, U.S. Pat.No. 4,328,646, an abrasion-resistant article is formed by subjecting amixture of hardcoating precursors to a glow discharge, and depositingthe product directly on a plastic substrate as a very thin film.However, inorganic hardcoatings such as silicon dioxide (SiO₂) depositeddirectly onto plastics such as polycarbonate have performance problemswhen the system is subjected to stresses produced by mechanical orthermal effects. These problems are due to the difference in propertycharacteristics of inorganic and plastic materials. For example, thethermal expansion coefficient for polycarbonate is about 7×10⁻⁵ m/m/°C., while the coefficient for Pyrex® glass is 3×10⁻⁶ m/m/° C. Thesedifferences result in tangential stresses at the interface of theplastic and the hardcoating which may in turn cause cracking of thehardcoating as a stress relief mechanism, especially when the article issubjected to various heating/cooling cycles. In attempting to alleviatethis problem, Hall et al. and Geffcken et al. in U.S. Pat. No(s).4,190,681 and 3,713,869, respectively, proposed the use of anintermediate layer to improve adhesion between the hard inorganic layerand the plastic layer. Furthermore, in copending application Ser. No.84,890, filed Apr. 6, 1987 for Devins et al. and assigned to theassignee of the present invention, now U.S. Pat. No. 4,842,941, there isdisclosed an intermediate layer which not only improves adhesion butalso provides a transition in properties from the plastic to theinorganic hardcoating, thus resulting in improved mechanical and thermalperformance.

There is a continuing interest in improving methods for forming articleshaving still greater abrasion resistance while also exhibitingimprovements in various other physical properties.

It is therefore an object of the present invention to provide a methodfor forming plastic articles having a high level of abrasion resistance,with improved resistance to cracking under exposure to thermal andmechanical stresses.

It is another object of the present invention to provide an improvedmethod for applying smooth, hard, transparent layers over athermoplastic substrate.

It is yet another object of the present invention to provide athermoplastic article having disposed thereover a protective top layercharacterized by uniform thickness, high abrasion resistance, andfreedom from pinholes and microcracks.

SUMMARY OF THE INVENTION

An improved method for forming an abrasion-resistant plastic article hasbeen discovered, comprising the plasma-enhanced chemical vapordeposition of a coating characterized by a gradual transition from acomposition consisting essentially of an interfacial material to acomposition consisting essentially of an abrasion-resistant material.The transition is achieved by gradually changing the feed composition ofthe coating material precursors, as described below.

Several different types of interfacial material may be used, as furtherdescribed below. Furthermore, many different abrasion-resistantmaterials capable of being applied by plasma-enhanced chemical vapordeposition (PECVD) may be used. "Interfacial" is meant herein todescribe a material situated between the substrate and theabrasion-resistant material and possessing some chemical characteristicsin common with each, as described in detail below.

Use of the method of the present invention for plastic articles such aspolycarbonates results in articles having all of the typical attributesof polycarbonates, such as high tensile and impact strength, while alsoexhibiting excellent abrasion resistance. Furthermore, good adhesiongenerally results between the polycarbonate substrate and the coatingformed thereon, which is also referred to herein as a "gradationallayer".

A further attribute of this method is that PECVD may be carried out asdisclosed herein at temperatures which are harmless to polycarbonate, incontrast to conventional chemical vapor deposition (CVD) processes whichrequire high operating temperatures often damaging to polycarbonatematerial. "Conventional" vapor deposition processes as used hereindenotes both CVD processes in which coating material precursors react inthe gas phase at elevated temperatures, typically above 400° C.; andalso denotes "physical vapor deposition" processes in which preformedcoating materials are simply evaporated onto a substrate. Theseprocesses do not involve the use of a plasma.

The scope of the present invention also includes an article comprising aplastic substrate and an abrasion-resistant gradational layer disposedthereon which consists essentially of an interfacial material at a depthclosest to the surface of the substrate, the relative concentration ofthe interfacial material gradually decreasing in a directionperpendicular to the substrate surface and being replaced by acorresponding concentration of an abrasion-resistant material.

DETAILED DESCRIPTION OF THE INVENTION

The article formed by the method of the present invention may includeany plastic material as a substrate. Illustrative plastics includeacrylic, polyester, polyethylene, polyimide, polyphenylene oxide,polycarbonate, polyamide, epoxy, phenolic,acrylonitrile-butadiene-styrene, and acetal. Blends of these materialsas well as blends with other materials such as impact modifiers are alsopossible. Furthermore, the substrates may contain various additives suchas UV absorbers, fillers, plasticizers, and the like.

Where transparency is required, the preferred substrate is formed ofpolycarbonate or an acrylic resin such as poly(methyl methacrylate).Polycarbonates are especially preferred materials for transparentsubstrates because of their excellent physical, mechanical and chemicalproperties. In general, the choice of substrate is ultimately determinedby the end use contemplated for the article.

Polycarbonates suitable for forming such a substrate are well-known inthe art and are described, for example, in U.S. Pat. No(s). 4,200,681and 4,210,699, both incorporated herein by reference, and in Devins etal., Ser. No. 034,890, filed Apr. 6, 1987, the contents of which arealso incorporated herein by reference. Such polycarbonates generallycomprise repeating units of the formula ##STR1## in which R is adivalent radical of a dihydric phenol, e.g., a radical of2,2-bis(4-hydroxyphenyl)-propane, also known as bisphenol A, ##STR2##

Polycarbonates within the scope of the present invention may be preparedby several well-known methods. For example, preparation may beaccomplished by reacting a dihydric phenol with a carbonate precursor. Awide variety of dihydric phenols, such as bisphenol A, may be used inthe present invention; many are disclosed in U.S. Pat. No(s). 2,999,835;3,082,365; 3,160,121; 3,334,154; and 4,190,681, all incorporated hereinby reference. Many carbonate precursors may be used; they are typicallyeither a carbonyl halide, a carbonate ester, or a haloformate. Exemplarycarbonate precursors are described in U.S. Pat. No. 4,190,681.

The term "polycarbonate" is meant herein to additionally include polymerblends of polycarbonates with various other materials such as polyestersand impact modifiers.

The substrate may be shaped into a variety of forms, depending on theend use contemplated for the articles. For example, a polycarbonate filmsubstrate may be formed by casting the molten polymer onto a flat openmold, and then pressing the material to a uniform thickness. Aftercooling, the film may then have a gradational layer applied thereover,as further described below. Furthermore, the substrate may be in theform of tubes, rods, or irregular shapes. When the article of thepresent invention is to be used as a glazing material, a polycarbonatematerial may be formed into flat or curved sheets by well-known methods,e.g., extrusion, injection molding, or thermoforming.

As mentioned above, the gradational layer which is applied over thesurface of a substrate according to the method of the present inventionis formed substantially of an interfacial material at a depth closest tothe surface of the substrate. For the purpose of clarification, theregion of the gradational layer containing at least about 99% by weightinterfacial material will sometimes be referred to herein as the"interfacial sublayer", while the region above the gradational sublayercontaining more than about 99% by weight of an abrasion-resistantmaterial will sometimes be referred to herein as the "abrasion-resistantsublayer". Furthermore, the region between the interfacial sublayer andthe abrasion-resistant sublayer will sometimes be referred to as the"gradational sublayer". The thickness of each layer is determined byprocess conditions, e.g., changes made in the gaseous reactant feed intothe PECVD reactor. Thus, the depth of each sublayer is predetermined bythe intended requirements for the particular abrasion-resistant article.For example, the abrasion-resistant sublayer may constitute a largerportion of the gradatonal layer when greater abrasion resistance isrequired.

The composition of the plasma-applied interfacial material of thepresent invention depends on the end use contemplated for the article.Organosilicons are particularly useful for forming the interfacialmaterial, especially when the abrasion-resistant material is silicondioxide. "Organosilicon" as used herein is meant to embrace organiccompounds in which at least one silicon atom is bonded to at least onecarbon atom, and includes silicone materials, as well as materialscommonly referred to as silanes, siloxanes, silazanes, andorganosilicones. Many of the organosilicons suitable for the method andarticle of the present invention are described in OrganosiliconCompounds, C. Eaborn, Butterworths Scientific Publications, 1960. Othersuitable organosilicon compounds are described in Organic PolymerChemistry, K. Saunders, Chapman and Hall Ltd., 1973.

Non-limiting examples of organosilicon compositions useful for thepresent invention are compounds represented by the general formula##STR3## wherein R¹ represents a monovalent hydrocarbon radical or ahalogenated monovalent hydrocarbon radical, Z represents a hydrolyzablegroup, and n may vary between 0 and 2. More specifically, Z ispreferably a member such as halogen, alkoxy, acyloxy, or aryloxy. Suchcompounds are well-known in the art and are described, for example, inS. Schroeter et al.'s U.S. Pat. No. 4,224,378, incorporated herein byreference.

Other exemplary organosilicons falling within the scope of the presentinvention include silanols having the formula

    R.sup.2 Si(OH).sub.3

wherein R² is selected from the group consisting of alkyl radicalscontaining from about 1 to about 3 carbon atoms, the vinyl radical, the3,3,3-trifluoropropyl radical, the gamma-glycidoxypropyl radical and thegamma-methacryloxypropyl radical, with at least about 70% by weight ofthe silanol being CH₃ Si(OH)₃. Such compounds are described in U.S. Pat.No. 4,242,381, incorporated herein by reference.

Preferred organosilicon compounds of the present invention arehexamethyldisilazane, hexamethyldisiloxane, vinyltrimethylsilane andoctamethylcyclotetrasiloxane.

When abrasion-resistant materials other than those containing siliconare to be employed, other classes of interfacial materials, such asvarious organometallics, would be appropriate. For example, titaniumisopropoxide, Ti₄ (O₃ H₇), could be a suitable interfacial material whentitanium dioxide is to be the abrasion-resistant material.

The interfacial material may alternatively comprise plasma-polymerizedacrylic materials. For example, an acrylic acid ester monomer ormethacrylic acid ester monomer may be vaporized and thenplasma-polymerized to form a polymeric coating which is deposited on theunderlying coating surface. Many of these materials are generallydescribed in the application of Devins et al., Ser. No. 034,890; in theEncyclopedia of Polymer Science and Technology, Volume I, IntersciencePublishers, John Wiley and Sons Inc., 1964, and in Chemistry of OrganicFilm Formers, by D. Solomon, John Wiley and Sons, Inc., 1967, as well asreferences cited in each of the texts. Other exemplary acrylic materialsare described in U.S. Pat. No. 4,239,798 and in 4,242,383, bothincorporated herein by reference.

The interfacial material may alternatively be a polyolefin. Nonlimitingexamples of suitable polyolefins include polyethylene, polypropylene,polyisoprene, and copolymers of these types of materials. Furtherincluded within the broad definition of polyolefin as used herein aresynthetic and natural elastomers, many of which are described in theEncyclopedia of Polymer Science and Technology, Vol. 5, pp. 406-482(1966), the disclosure of which is incorporated by reference herein.Many of these materials can be deposited according to the presentinvention by vaporizing and then plasma-polymerizing their monomerprecursors under the plasma conditions described below.

Nonlimiting examples of compounds suitable for the abrasion-resistantmaterial include silicon dioxide, silicon nitride, silicon oxynitride,silicon carbide, silicon carbonitride, boron oxide, boron nitride,aluminum oxide, aluminum nitride, titanium dioxide, tantalum oxide, ironoxide, germanium oxide, and germanium carbide. Mixtures of suchmaterials are also possible. When the article is to be used as a glazingmaterial, a silicon dioxide top layer is preferred because of its easeof plasma deposition, its excellent transparency, and the relativelyinexpensive cost of its precursors. It should be understood that"precursor" as used herein is meant to include either one precursor ormore than one precursor, depending on the particular materials beingused.

A primer may be applied to the surface of the substrate prior to theapplication of the gradational layer. The primer may be applied byconventional methods well-known in the art, e.g., spraying, rollcoating, curtain coating, dip coating, brushing, and otherart-recognized techniques. This layer tends to increase the adhesion ofthe interfacial material to the substrate surface, while also acting asan incorporation site for one or more ultraviolet light (UV) absorbers.The primer material generally exhibits some compositional differencesfrom the interfacial material.

Various well-known materials may be used to form the primer, with theproviso that they be chemically compatible with both the substrate andthe gradational layer material. Among the suitable primer materials forpolycarbonate substrates are thermoplastic and thermoset acrylicpolymers, as described in the Devins et al. application mentioned above.

Preferred acrylic materials for the primer are those which areultraviolet light-curable. These materials are typically applied to thesubstrate as a monomer. An exemplary composition of this type comprises:

(A) at least one polyfunctional acrylate monomer represented by thegeneral formula ##STR4## wherein n is an integer having a value of from1 to 4, and R³ is selected from the group consisting of aliphatichydrocarbon groups, an aliphatic hydrocarbon group containing at leastone ether linkage, and a substituted aliphatic hydrocarbon groupcontaining at least one ether linkage; and R' is selected from hydrogenor lower alkyl radicals;

(B) colloidal silica,

(C) at least one acryloxy functional silane of the formula ##STR5##wherein R⁴ is a monovalent hydrocarbon radical, R⁵ is a divalenthydrocarbon radical, R⁶ is selected from the group consisting ofhydrogen atoms and monovalent hydrocarbon radicals, x is an integer offrom 1 to 4 inclusive; and

(D) a photoinitiator.

After the composition is applied to the substrate, it is exposed toultraviolet light for a period of time sufficient to polymerize andcrosslink the polyfunctional acrylate monomers, thereby forming a curedcoating. Ketones are useful as initiators when curing the acryliccompositions in inert atmospheres such as nitrogen, while blends of atleast one ketone and at least one amine are useful as initiators whencuring in oxygen-containing atmospheres, as described in R. Chung's U.S.Pat. No. 4,478,876, incorporated herein by reference.

Many of the organosilicon materials discussed above are also suitable asprimers (not applied by PECVD), and in that instance, they may oftenhave colloidal silica dispersed therein, which increases the hardness ofthe material. Dispersions of colloidal silica in organosilicon materialsare well-known in the art, and are described, for example, in U.S. Pat.No(s). 3,986,997, 4,027,073, 4,239,798, 4,284,685, 4,436,851, allincorporated herein by reference. Typically, the colloidal silica isdispersed in an aqueous solution of the organosilicon. For example,these compounds may comprise a dispersion of colloidal silica in a loweraliphatic (e.g., less than about 6 carbon atoms) alcohol-water solutionof the partial condensate of a silanol.

When used, colloidal silica should comprise about 5% to about 40% byweight of the total nonvolatile weight of the primer. Furthermore,aqueous colloidal silica dispersions used in the present inventiongenerally have a particle size in the range of about 5 to about 150nanometers in diameter. An especially preferred particle size range isfrom about 5 to about 20 nanometers in diameter.

An especially preferred colloidal silica-containing organosiliconmaterial for use as the primer is described in B. Ashby et al.'s U.S.Pat. No. 4,374,674, incorporated herein by reference, and comprises:

(a) a dispersion of colloidal silica in a solution of the partialcondensate of a silanol having the formula RSi(OH)₃ or R² Si(OH)₂,wherein R is selected from the group consisting of alkyl groups havingabout 1 to 3 carbon atoms and aryl groups having about 6 to 20 carbonatoms, wherein at least 70 weight percent of the silanol is CH₃ Si(OH)₃or (CH₃)₂ Si(OH)₂ in a mixture of an aliphatic alcohol and water,

said dispersion containing from 10 to 50 percent by weight of solids,said solids consisting essentially of 10 to 70 percent by weight of thecolloidal silica and 30 to 90 percent by weight of the partialcondensate, and

(b) an effective amount of an ultraviolet light absorbing agentcomprising a compound having the formula ##STR6## wherein:

X is ##STR7##

Y is H or OH;

Z is H, OH, OQ or OW, where at least one Z is OH if Y is H;

Q is -CH₂ (CH₂)_(n) Si(R²)_(x) (OR¹)₆ ; and

W is -C_(m) H_(2m+1) ;

where x=0, 1 or 2, y=1, 2 or 3, x+y=3, and R¹ is an alkyl or alkanoylgroup having about 1 to 6 carbon atom, R² is an alkyl group having fromabout 1 to 6 carbon atoms, n=0, 1 or 2 and m=1 to 18. The compositionforming this material typically contains sufficient acid to provide a pHin the range of about 3.0 to 7.0. The Ashby et al. patent also describesmethods of applying and curing these coatings.

Exemplary condensates of R₂ Si(OH)₂ -type silanols, and compositionsformed therefrom, are disclosed in U.S. Pat. No. 4,159,206, incorporatedherein by reference.

Another preferred organosilicon material for use as the primer comprisesa water/aliphatic alcohol dispersion of ammonium hydroxide-stabilizedcolloidal silica and a partial condensate derived from organotrialkoxysilanes. Such a material is described by B. Anthony in U.S. Pat. No.4,624,870, incorporated herein by reference, and is preferably used atan alkaline pH, i.e., a pH of at least about 7.1.

Exemplary UV absorbers which may be incorporated into the primer arethose of the hydroxy benzophenone and benzotriazole type, although otherUV absorbers might also be used. When a UV-curable primer material isemployed, latent UV absorbers which do not interfere with the curingreaction should be used. These types of UV absorbers are known in theart and are described, for example, in Chung et al. U.S. Pat. No(s).4,372,835, and 4,478,876 and Olson et al. U.S. Pat. No. 4,455,205, allincorporated herein by reference. An example of a latent UV absorber isresorcinol monobenzoate.

The amount of UV absorber depends in part on the particular compositionof the acrylic, and in part on whether a UV absorber is also present inthe substrate material itself. Those skilled in the art will be able todetermine an appropriate quantity without undue experimentation.

Other additives which may be incorporated into the primer includeanti-oxidants, fillers, reinforcing agents, wetting agents, and thelike.

The gradational layer may be applied on the substrate or "over" thesubstrate, i.e., onto the surface of a primer coating disposed on thesubstrate. The application is accomplished by PECVD, which in general isa method of applying films from a gaseous discharge to a substrate. Forexample, the Kirk-Othmer Encyclopedia of Chemical Technology, Volume 10,discusses the plasma deposition of inorganic materials. Furthermore,details regarding the plasma deposition of inorganic thin films aregiven in Thin Film Processes, Ed. by Vossen and Kern, Academic Press,1978. Exemplary plasma deposition methods are also described in U.S.Pat. No(s). 4,096,315, 4,137,365, 4,361,595, and 4,396,641. While all ofthe above-listed references generally describe plasma deposition, theprocess disclosed herein must be carried out according to the variousoperating parameters discussed below in order to obtain an articlehaving excellent abrasion resistance, optical properties, and adhesionbetween its layers.

The following general statement regarding the operation of PECVD for thepresent invention applies to both the deposition of the interfacialmaterial and the abrasion-resistant material. When a discharge isproduced at low pressure in the film-forming reactants, the reactantsbecome ionized, forming a plasma. A portion of the material is in theform of ions, electrons, and atomic free radicals generated in theplasma prior to formation of the film over or upon the substrate. Mostof the reactive species consist of the atomic free radicals. Althoughthe inventors do not wish to be bound by a specific theory, it isthought that at the higher plasma frequencies, e.g., 13.56 MHz, and atthe typical gas pressures employed, e.g., 1 Torr, most of the filmformation on or over the substrate occurs when the free radical speciesdiffuse out of the plasma to the deposition surface. Thus, free radicalsreact on or over the primed or unprimed substrate to form the desiredlayer. A distinct advantage of PECVD over conventional chemical vapordeposition processes lies in the fact that the applied electric fieldenhances free radical formation, thereby permitting the use ofdeposition temperatures which are low enough to prevent damage tosubstrates such as polycarbonates, i.e., temperatures less than about130° C. Furthermore, when used under the process conditions disclosedherein, PECVD can be carried out with a much higher percentage of freeradicals than is possible with conventional CVD.

One PECVD system suitable for the process disclosed herein is designatedas Model 2411 and sold by PlasmaTherm, Inc. However, in order to achievethe excellent results obtained by the present invention, use of this orany other PECVD apparatus must fall within the processing andcompositional parameters disclosed herein.

In applying the gradational layer by PECVD, the primed or unprimedsubstrate is placed in a reactor chamber in which an electric field canbe generated. The reactor chamber must be capable of being substantiallyevacuated, i.e., to a pressure of less than or equal to about 1.0millitorr.

The method of generating and applying the electric field is not criticalto this process. For example, the field may be generated by inductivecoupling systems, as described, for example, by J. Vossen in GlowDischarge Phenomena in Plasma Etching and Plasma Deposition, J.Electrochemical Society, Feb. 1979, pp. 319-324.

A capacitively coupled system may also be used to generate an electricfield, and is preferred for use in the present invention. By thistechnique, which is generally described in the Vossen article referredto above, two plasma is formed therebetween. Each electrode may be aplate of a material that is a good electrical conductor, e.g., aluminum.The electrodes preferably each have a planar face parallel to the otherelectrode.

In preferred embodiments of the present process wherein the capacitivelycoupled system is utilized, the electrodes are horizontally arranged,i.e., an upper electrode is affixed in the upper region of the reactorchamber with a planar surface facing a planar surface of a lowerelectrode affixed in the lower region of the vacuum chamber. The spacingbetween the electrodes depends on the desired strength of the appliedelectric field, as well as the size of the article being coated. Thoseskilled in the vapor deposition art appreciate the interrelationship ofthese processing variables and are therefore able to make adjustmentsfor a particular use of this invention without undue experimentation. Inpreferred embodiments, the substrate is positioned on the surface of thelower electrode which faces the upper electrode, such that the substratesurface to be coated is parallel to the facing surface of the upperelectrode. Alternatively, the electrodes might be arranged vertically oralong other geometric planes within the chamber as long as a plasma canbe generated therebetween.

Film-forming materials must be in vapor or gaseous form for the PECVDprocess. Vapor reactants, such as acrylic, olefinic, or organosiliconemonomers, are vaporized from the liquid form prior to entry into thereactor chamber. A preferred technique when sufficient vapor pressuresare difficult to obtain is to introduce a mist of the liquid into theplasma region.

In preferred embodiments, the liquid material may be degassed by coolingit and then subjecting it to a vacuum. Depending on its particularboiling point, the liquid is then heated to ambient temperature orhigher in order to provide sufficient positive vapor pressure to flowthrough a channeling system such as that described below. Alternatively,a carrier gas such as helium can be blown through the liquid to obtain adiluted vapor mixture of desired composition.

Gaseous reactants such as silane or nitrous oxide are suitable innatural form for reaction in the plasma, alone or with a carrier gas toinsure proper metering into the reactor chamber. Sometimes, e.g., in thecase of nitrous oxide, the reactants may be stored in liquid formbeforehand.

The reactor chamber is evacuated prior to entry of the gaseousreactants. Chamber pressures as required for the process of the presentinvention range from about 50 millitorrs to about 10 Torrs, with apreferred pressure being in the range of about 0.3 Torr to about 1.0Torr.

The gaseous reactants which form the composition of the gradationallayer may be supplied from an external source through a series of inletpipes into the reactor chamber. The technical particularities ofchanneling the various gases into the reactor chamber are well-known inthe art and need not be described in detail here. For example, each gasinlet may be connected to a central feed line which carries the gasesinto the reactor chamber. In preferred embodiments, gaseous reactantsfor the abrasion-resistant composition are mixed with a carrier gas suchas helium to improve the flow of the reactants into the chamber. Theflow of carrier and reactant gases into the reactor may be governed bymass flow controller valves which are well-known in the art and whichserve to both measure the flow of gases and to control such flow.Furthermore, the carrier gas, when used, may be premixed with thegaseous reactants or may be fed into the central feed line by a separateinlet. For example, when silane (SiH₄) is used as a reactant for formingsilicon dioxide, it may be premixed with helium in a SiH₄ /He volumeratio ranging from about 2:98 to 20:80. Although a carrier gas is notcritical to the present invention, its use improves the uniformity ofplasma density and gas pressure within the reactor chamber. Furthermore,use of the carrier gas tends to prevent gas phase particulation of theplasma-formed coating material, and also improves film quality in termsof transparency (when desired) and abrasion resistance.

Formation of the gradational layer is facilitated by the use of separateinlet pipes for reactants forming the interfacial material and forreactants forming the abrasion-resistant material. The flow of each ofthese gases is also controlled by the mass flow controller valvesdescribed above. Since the interfacial material is often formed fromreactants which are liquids at room temperature, the material isadvantageously stored in a supply vessel located in an oven to allow forthe vaporization of the material prior to entry into the reactorchamber.

When using the capacitively coupled system, the gaseous reactantsentering the reactor chamber from the central feed valve are passedbetween the upper and lower electrodes and over the substrate to becoated. The quality of the gradational coating on or over the substrateor primer depends greatly on both the flow rate of the reactants and theflow dynamics, i.e., laminar characteristics, as described below. Forexample, excessive flow rates would force the active, film-formingreactants past the zone above the deposition surface before they reactto form the coating on the surface. Conversely, if the flow rate is toosmall, the film-forming reactants will quickly be depleted and therebylead to nonuniformities in film thickness. The flow rate of interfacialmaterial reactants may range from about 5 sccm to about 250 sccm, withabout 20 sccm to about 100 sccm being preferred. For coating surfaceslarger than about 10 square feet, which might require reactor chamberslarger than the PlasmaTherm reactor described below, higher flow ratesmay be desirable, e.g., up to about 2000 sccm. As further describedbelow, the interfacial material reactants may be passed into the reactorchamber with a carrier gas.

The individual flow rates of reactants forming the abrasion-resistantmaterial range from about 500 sccm to about 10,000 sccm for eachreactant when a carrier gas is used, and from about 5 sccm to about 2000sccm without a carrier gas. For example, a silicon dioxide coating mayadvantageously be formed by flowing silane at a rate of about 10 sccm toabout 100 sccm and nitrous oxide at a rate of about 300 sccm to about5000 sccm into the reactor along with a carrier gas flowing at aconstant value in the range between about 500 sccm and 5000 sccm. As inthe case of the interfacial material precursor flow rates, higherabrasion-resistant material precursor flow rates may be desirable forcoating surfaces larger than about 10 square feet. For example, informing silicon dioxide, silane flow rates up to about 250 sccm, nitrousoxide flow rates up to about 8000 sccm, and an increase in carrier gasflow proportional to the increase in silane flow might be used. Those ofordinary skill in the art will be able to easily select a proper flowrate for a particular substrate and coating material if the teachingsherein are followed.

While gas flow, gas pressure, and plasma power may be varied within theranges described above in order to suit the requirements of a particularend use, it may be desirable in some embodiments to maintain these threeparameters as fixed values during formation of the gradational layer inorder to maintain a steady plasma. Preferred embodiments also call foreach gaseous reactant passing into the reactor chamber to be mixed witha carrier gas which flows at a constant rate throughout plasmadeposition.

Preferred embodiments also call for the total gas flow into the reactorchamber to be a constant amount during the deposition of the gradationalcoating. This should not be viewed as an absolute requirement for goodquality coatings, but as a more efficient means for process control.

Laminar flow of the gaseous reactants relative to the deposition surfaceis of great importance to the present invention because it enhances theuniformity of the coating in terms of thickness and properties such ashardness, clarity, and, for the interfacial material, adhesive andthermal expansion compensation capabilities.

"Laminar flow" as used herein is defined as smooth and steady flow,i.e., a substantially streamlined flow of gaseous reactants relative tothe substrate and characterized by the absence of turbulent flow ofreactant molecules. This type of gas flow is described, for example, inFluid Mechanics, by F. White, McGraw-Hill Book Company, 1979, p. 305 etseq., the disclosure of which is incorporated herein by reference. Asdescribed in the White text, laminar flow may be generally characterizedby a Reynolds value of between about 1 and 1000. In preferredembodiments of this invention, a particularly preferred Reynolds valueis about 2.5. Those skilled in the art understand that small areas ofturbulence may be present, but do not significantly affect theproperties of the deposited coating. Furthermore, as pointed out above,the mass flow of each gas may be regulated by adjustment means tocontrol the laminar flow characteristics of the gaseous reactants.

In preferred embodiments, the coating surface is heated to a temperaturebetween about 100° C. and 130° C. during plasma deposition, 100° C.being the most preferred temperature. The heating can be accomplished bya variety of well-known methods. For example, the resistively-heatedlower electrode upon which the substrate rests serves to provide heat tothe coating surface through the substrate. In some embodiments of thisinvention, coating surface temperatures of 100° C. or higher increasethe deposition rate of the abrasion-resistant material onto theunderlying surface. Furthermore, the elevated temperature may alsoresult in greater abrasion resistance. It should also be understood thatdeposition onto a coating surface maintained at between about roomtemperature and 100° C. is also within the scope of this process.

In preferred embodiments of this invention, the substrate surface may becleaned by washing with an alcohol solvent such as isopropanol prior toapplication of the next layer. This step removes dirt, contaminants, andadditives such as wetting agents from the surface. The primer surfacemay also be washed in this manner.

After being washed, the substrate is vacuum-desiccated by well-knownmethods to remove any water on or in the surface region which wouldinterfere with the adhesion of the subsequently-deposited layers. Thedesiccation treatment may also be used on the primer surface after ithas been applied to the substrate. Desiccation temperatures range fromabout ambient temperature to about 120° C., with the preferred rangebeing about 80° C. to about 90° C. Desiccation duration ranges fromabout 2 hours to about 16 hours, with longer times within this rangecompensating for lower temperatures, and vice versa.

The surface of the substrate can often be etched after placement in thereaction chamber. Etching techniques, which in general are well-known inthe art, may also be used to treat the primer surface to create freeradical species thereof which will later bond with the free radicalspecies of the plasma-applied gradational material, thereby improvingadhesion between these layers.

As the reactants enter the reaction chamber after the coating surface istreated as described above, an electric field is generated underpreselected frequency and power conditions to ionize the gas mix,thereby forming a plasma. Methods of generating an electric fieldbetween electrodes are well-known in the art and therefore do notrequire an exhaustive description here. A dc field, or an ac field from50 Hz to about 10 GHz, may be used. Power values range from betweenabout 10 watts to 5000 watts. A particularly suitable electricalfield-generating means for this process is the use of a high frequencypower supply to initiate and sustain the plasma. When such a powersupply is used, a preferred operating frequency is 13.56 MHz, asdescribed, for example, in R. Kubacki's U.S. Pat. No. 4,096,315,incorporated herein by reference. The particular frequency and powervalues utilized will depend in part on the particular depositionrequirement for the coating material. For example, when organosiliconemonomers are reacting in the plasma, lower frequencies and higherelectrical power values within the above-described ranges increase thepolymerization rate and deposition rate of the material, especially whenlower chamber pressures within the above-mentioned range are alsoemployed.

An additional refinement, well-known in the art, which offers thepotential for beneficially modifying the plasma (e.g., by increasing theionization and providing improved spatial control of the plasma), usesseparate magnetic fields in conjunction with the electric field. Anexample of such magnetic enhancement is "ECR" (electron cyclotronresonance) microwave plasma technique.

As mentioned above, the gradational layer may be formed by initiallyfeeding plasma-polymerizable interfacial material precursors into thereactor, and then gradually changing the feed composition toabrasion-resistant material precursors. The change in feed compositionmay be accomplished by manually adjusting the flow of each gas into thecentral feed line. Those skilled in the art appreciate that such gasflow adjustment can also be accomplished automatically by various means.Each adjustment is made according to a prescribed time and flow rateregimen based on data obtained from the mass flow controller valves.

In preferred embodiments, the PECVD deposition of the gradational layeroccurs in three stages: a first stage in which only the interfacialmaterial precursor is fed into the reactor and plasma-polymerized; asecond stage in which the interfacial precursor flow is graduallyreduced while the flow of abrasion-resistant material precursors isinitiated and gradually increased; and a third stage in which only theabrasion-resistant material precursors are fed into the reactor anddeposited. A carrier gas is often used during each stage of thedeposition. The length of each stage is determined by the desiredthickness of each sublayer. The resulting gradational layer has asublayer of interfacial material closest to the substrate, a sublayer ofabrasion-resistant material farthest from the substrate, and agradational sublayer therebetween which is characterized by a gradualtransition from the interfacial material to the abrasion-resistantmaterial. The change in feed composition may be effected linearly ornonlinearly, e.g., exponentially, from the interfacial precursor flow tothe abrasion-resistant precursor flow. The examples which follow furtherdescribe this technique.

It is also within the scope of this invention that the initial gascomposition flowing into the reactor contain a small amount ofabrasion-resistant precursor material, e.g., about 0.1% of the total gasflow, the remainder of the composition comprising interfacial materialprecursors. The abrasion-resistant precursor composition is thengradually increased in proportion to the gradual decrease in theinterfacial material precursor composition, resulting in a gradationallayer characterized by a gradual transition from a compositionconsisting essentially of an interfacial material to a compositionconsisting essentially of an abrasion-resistant material.

The overriding consideration for feed composition adjustment is, ofcourse, the desired characteristics of the deposited gradational layer.For example, an article requiring an especially high level ofabrasion-resistance but not likely to be subjected to rapid thermalchanges or wide temperature variations may be formed by decreasing thetime period of interfacial material precursor flow and increasing thetime period of abrasion-resistant material precursor flow. The resultingarticle would thus have a thicker abrasion-resistant layer than anarticle formed according to the regimen exemplified above.

Conversely, an article likely to be subjected to wide temperaturevariations may be formed by decreasing the time period ofabrasion-resistant precursor flow and increasing the time period ofinterfacial material precursor flow to produce an article having more ofits depth as interfacial material.

The thickness of the gradational layer is in part determined by thecontemplated end use of the article, and generally may range from about0.01 micron to about 5.0 microns. Similarly, the thickness of each zoneor sublayer --when distinctly present--depends on the end use of thearticle.

After passing over the coating surface, the carrier gas and any gasreactants or products which have not been deposited on the substratesurface may be directed out of the chamber through an exit valve andthen to a gas pumping and exhaust system. Means for expelling theseexcess materials from the chamber are well-known in the art. When theelectrodes are circular and flat as described above, the exhaustmanifold can be located in the center of the lower electrode.Furthermore, after the application of the gradational layer, residualgases may be removed from the reactor chamber by pumping means.

Embodiments of the present invention result in the formation of articleshaving a high degree of hardness and an abrasion resistance.Furthermore, when the process is utilized to form a transparent glazingmaterial, the resulting articles are very smooth and free frommicrocracks. Moreover, the gradational layer is capable of accommodatinglarge differences in thermal expansion when the article is subjected toheating/cooling cycles.

EXAMPLES

The following examples are provided to more fully describe the presentinvention. It is intended that these examples be considered asillustrative of the invention, rather than limiting what is otherwisedisclosed and claimed herein.

A brief description of the tests utilized in some or all of thefollowing examples will now be given:

Abrasion resistance was measured by a combination of two ASTM testmethods.The Taber Abrasion Test, ASTM D1044, was used with a 1,000 gramtotal weight load evenly distributed on the two wear wheels. 300 and/or1,000 cycles were used, as indicated below. The second test method wasASTM D1003, which uses a Gardner Hazemeter, Model UX 10. In this method,the percentage of light scattering is measured before and after thespecimen is taber-abraded. The lower the value, the better the abrasionresistance and hardness.

Optical transparency was measured on a UV-Visible Spectrometer, Model330, manufactured by the Perkin Elmer Corporation.

Adhesion was measured by the scribed adhesion test, ASTM Test D3359, inwhich a 0.75 inch (1.9 cm) square of the material is cross-hatched into2.0 mm squares. A 3M Company No. 610 adhesive tape is then pressed ontothe surface of the grid pattern and removed with a swift, even pull. Theamount of material remaining on the sample is indicative of theadherence characteristics of the coating to an underlying surface.

Two types of temperature cycling tests were carried out. Test A was verysevere because of the large temperature excursion and very abrupt rateof temperature change (dT/dt). The thermal cycle profile consisted oftwo stages: first, a cool-down to -35° C. (dT/dt=22° C./min); hold for90 minutes; heat up to 50° C. (dT/dt=17° C./min); hold for 90 minutes;cool down to 20° C. (dT/dt=26° C./min);hold for 15 minutes, and thenexamination of the sample; and second, cool down to -35° C. (dT/dt=22°C./min); hold for 90 minutes, heat up to 100° C. (dT/dt=15° C./min);hold for 90 minutes; cool down to 20° C. (dT/dt=30° C./min); hold for 15minutes,and then examination of the sample.

Test B consisted of ten cycles of the following thermal cycle: cool down-35° C.; hold for 120 minutes, heat up to 85° C., hold for 120 minutes;cool down to -35° C., etc. In this case, the rate of temperature changewas substantially lower than in Test A, and was held constant throughoutthe entire ten cycles at dT/dt=1.41° C./min.

Strain to microcracking measurements were made on 4"×1/2"×1/4" samples.For this purpose the samples were placed in a three point bendingjigattached to an Instron device. The latter bent the samples andrecordedthe sample deflection at the time microcracking was visuallyobserved. The strain to microcracking, ε, was then calculated from ε=4dlT/L², where dl is the deflection at microcracking, L the length of thesample (4"), and T, its thickness (1/4").

Impact strength was determined by the use of a Gardner Heavy-DutyVariable Impact Tester.

The thickness of the coating applied to the substrate by plasmadeposition was controlled and determined by process conditions andprocessing time, as described above. Once the reactant gas mix flowrate, substrate temperature, frequency, and pressure have been set,thickness can be determined within about ±5% by simply timing theduration of the process.

The thickness uniformity of an applied coating is assessed from theinterference color produced by the coating; such a method is suitablefor coatings having thicknesses of about 0.3 microns. For greatercoating thicknesses (from about 0.4 micron-10 microns), a profilometer(Sloan Dektak II) provides a determination of coating uniformity. Small,thin silicon wafers are positioned at strategic locations prior todeposition of the coating and then removed afterwards, exposing thesteps used for measuring thickness.

EXAMPLE 1

Using the processing conditions shown in Table 1, a gradational layerwas deposited on bisphenol A-based polycarbonate (samples 1 and 2). Theabrasion-resistant material was SiO₂ and the interfacial materialwasplasma-polymerized vinyltrimethylsilane (VTMS).

                  TABLE 1                                                         ______________________________________                                        (Samples 1 and 2)                                                                       Pre-       Process Conditions                                       Sublayer  calculated (Pressure,    Time of                                    Composition                                                                             Thickness  flow rates, power)                                                                          Gas Feed                                   ______________________________________                                        SiO.sub.2 0.7 μm  1000 mTorr    20 min                                                          1200 sccm SiH.sub.4 (He)                                                      800 sccm N.sub.2 O                                                            50 watts                                                 Gradational                                                                             0.6 μm  1000 mTorr    20 min                                                          (Composition varied                                                           linearly)                                                                     50 watts                                                 VTMS*     1000 A     1000 mTorr    20 min                                                          40 sccm VTMS                                                                  1960 sccm He                                                                  50 watts                                                 ______________________________________                                        *Vinyltrimethylsilane                                                     

The linear variation of composition for the gradational sublayeroccurred as follows:

                  TABLE 2                                                         ______________________________________                                        Time of                                                                       Gas Feed                                                                              SiH.sub.4 Flow                                                                          N.sub.2 O Flow                                                                          VTMS Flow                                                                              He Flow                                  (minutes)                                                                             (sccm)    (sccm)    (sccm)   (sccm)                                   ______________________________________                                        20      0          0        40       1960                                     22.5    150       100       35       1680                                     25      300       200       30       1440                                     27.5    450       300       25       1200                                     30      600       400       20       960                                      32.5    750       500       15       720                                      35      900       600       10       480                                      37.5    1050      700        5       240                                      40      1200      800        0       0                                        ______________________________________                                    

Based on measurements on the gradational coatings deposited onto silicon(Si) wafers at strategic locations in the reactor, it was concluded thatthe gradational coatings had good thickness uniformity. The coatingswere also completely transparent, as demonstrated by their appearance,and alsofrom absorption measurements made in the visible region (400-800nm). In the UV region, below 400 nm, the measured absorption paralleledthat of the polycarbonate.

Taber abrasion measurements carried out on sample 1 showed animprovement as compared to bare polycarbonate.

Thus, the increase in haze after 300 cycles was 20-40%, which isessentially that of polycarbonate after 50 cycles.

The effect of temperature cycling of sample 2, using Test B as describedabove, is show: in Table 3 and compared with data obtained for controlsample 3, a structure made by depositing SiO₂ onto polycarbonatedip-coated with an organosilicone primer comprising a dispersion ofcolloidal silica in a solution of the partial condensate of an alkylsilanol which further included a UV screening agent. The thickness ofthe organosilicone material after heat-curing was about 5.0 microns. Thegradational structure shows a distinct improvement in the temperaturecycling performance.

                  TABLE 3                                                         ______________________________________                                        Temperature Cycling, Test B                                                         Thickness (μm)                                                       Sample         VTMS     Gradational                                                                            SiO.sub.2                                    No.   Primer*  Sublayer Sublayer Sublayer                                                                             Result                                ______________________________________                                        2     --       0.1      0.6      0.7    No                                                                            micro-                                                                        cracks                                3     5        --       --       4.0    Micro-                                                                        cracked                               ______________________________________                                        *Organosilicone                                                           

EXAMPLE 2

Using the processing conditions shown in Table 4, a gradational layerformed from the same precursors as in Example 1 was deposited onbisphenolA-based polycarbonate (sample 4). The gradational layer wasalso applied onpolycarbonate material which had first been dip-coatedwith an organosilicone material comprising a dispersion of colloidalsilica in a solution of the partial condensate of an alkyl silanol whichfurther included a UV screening agent (sample 5). The thickness of theorganosilicone material after heat-curing was about 5.0 microns.

                  TABLE 4                                                         ______________________________________                                        (Samples 4 and 5)                                                                       Pre-       Process Conditions                                       Sublayer  calculated (Pressure,    Time of                                    Composition                                                                             Thickness  flow rates, power)                                                                          Gas Feed                                   ______________________________________                                        SiO.sub.2   2 μm  1000 mTorr    40 min                                                          2500 sccm SiH.sub.4 (He)                                                      1650 sccm N.sub.2 O                                                           50 watts                                                 Gradational                                                                             1.2 μm  1000 mTorr    40 min                                                          (Composition varied                                                           linearly)                                                                     50 watts                                                 VTMS*     50 A       1000 mTorr     2 min                                                          100 sccm VTMS                                                                 2400 sccm He                                                                  50 watts                                                 ______________________________________                                        *Vinyltrimethylsilane                                                     

The linear variation of composition for the gradational sublayeroccurred as follows:

                  TABLE 5                                                         ______________________________________                                        Time of SiH.sub.4 Flow                                                                          N.sub.2 O Flow                                                                          VTMS Flow                                                                              He Flow                                  Gas Feed                                                                              (sccm)    (sccm)    (sccm)   (sccm)                                   ______________________________________                                         2 min. 0         0         100      2400                                     12 min. 625       408       75       1800                                     22 min. 1250      816       50       1200                                     32 min. 1875      1235      25       600                                      42 min. 2500      1625      0        0                                        ______________________________________                                    

As in Example 1, the coatings were very uniform. Furthermore, theiropticalcharacteristics were excellent.

Supporting evidence of a gradational structure was obtained fromSecondary Ion Mass Spectrometry measurements. The device used was asecond generation Cameca IMS-3F ion microscope. These measurements werecarried out on a gradational coating deposited on a silicon wafersimultaneously with the deposition made on samples 4 and 5. Thegradational portion of the structure had a gradual decrease in thecarbon content from the polycarbonate surface to the SiO₂ layer, whereit was essentially zero.

Taber measurements showed that sample 4 possessed even greater abrasionresistance than sample 1. The increase in haze after 300 cycles was only8%.

The scribed adhesion test showed 80% removal of the SiO₂ from thegradational layer. However, since the tape sticks more strongly to anSiO₂ surface than to a typical organosilicone surface, the adhesion isconsidered to be much better than indicated by the test.

The effect of temperature cycling on sample 5, using Test A as describedabove, is shown in Table 6 and compared with data obtained on structures(samples 6 and 7) made by depositing SiO₂ on polycarbonate precoatedwith the same organosilicone. Again, the gradational structureoutperformed the non-gradational structures, even when the SiO₂ sublayerwas quite thin (sample 7).

                  TABLE 6                                                         ______________________________________                                        Temperature Cycling - Test A                                                        Thickness (μm)                                                                    Grada-        Result                                                            VTMS    tional                                                                              SiO.sub.2                                                                           1st    2nd                                 Sample         Sub-    Sub-  Sub-  Exami- Exami-                              No.   Primer*  layer   layer layer nation nation                              ______________________________________                                        5     5        0.05    1.2   2.0   O.K.   A few                                                                         micro-                                                                        cracks at                                                                     edges                               6     5        --      --    2.0   O.K.   Micro-                                                                        cracked                             7     5        --      --    0.3   O.K.   Micro-                                                                        cracked                             ______________________________________                                        *Organosilicone                                                           

Table 7 below demonstrates that the gradational layer does not affectthe properties of the underlying substrate, such as impact strength.Sample 5,as mentioned above, was gradationally coated according to thepresent invention. Control sample 7(a) was uncoated bisphenol A-basedpolycarbonate. Control sample 7(b) was the same polycarbonate materialdip-coated with the organosilicone used for sample 5.

                  TABLE 7                                                         ______________________________________                                        Impact Strength                                                               Thickness (μm)           Impact                                            Sample         VTMS     Gradational                                                                            SiO.sub.2                                                                            Strength                              No.   Primer*  Sublayer Sublayer Sublayer                                                                             (in./lb.)                             ______________________________________                                        5**   5        0.05     1.2      2.0    >320                                  7(a)  --       --       --       --     >320                                  7(b)  5        --       --       --     >320                                  ______________________________________                                        *Organosilicone                                                               **After thermal cycling                                                   

Upon impact, cracking of the coating occurred in the immediate vicinityof the impact area, but no cracking or delamination occurred elsewhere.

EXAMPLE 3

Using the processing conditions and compositions shown in Table 8, agradational coating was deposited on bisphenol A-based polycarbonate(sample 8), and on the same polycarbonate dip-coated with anorganosilicone material comprising a dispersion of colloidal silica in asolution of the partial condensate of an alkyl silanol which furtherincluded a UV screening agent (sample 9). The thickness of thisorganosilicone material after heat-curing was about 5.0 microns.

Samples 10 and 11 were controls. Sample 10 was formed by PECVD ofSiO₂directly onto polycarbonate. Sample 11 was formed by PECVD of SiO₂onto polycarbonate which had been dip-coated with an organosilicone ofthetype described in Example 2.

                  TABLE 8                                                         ______________________________________                                        (Samples 8 and 9)                                                                       Pre-       Process Conditions                                       Sublayer  calculated (Pressure,    Time of                                    Composition                                                                             Thickness  flow rates, power)                                                                          Gas Feed                                   ______________________________________                                        SiO.sub.2 2.5 μm  1000 mTorr    48 min                                                          2500 sccm SiH.sub.4 (He)                                                      1625 sccm N.sub.2 O                                                           50 watts                                                 Gradational                                                                               1 μm  1000 mTorr    40 min                                                          (Composition varied                                                           exponentially)                                                                50 watts                                                 VTMS*     50 A       1000 mTorr     2 min                                                          175 sccm VTMS                                                                 2500 He                                                                       50 watts                                                 ______________________________________                                        *Vinyltrimethylsilane                                                     

The variation in composition for the gradational sublayer wasapproximatelyexponential and occurred as follows:

                  TABLE 9                                                         ______________________________________                                        Time of                                                                       Gas Feed                                                                              SiH.sub.4 Flow                                                                          N.sub.2 O Flow                                                                          VTMS Flow                                                                              He Flow                                  ______________________________________                                         2 min. 0         0         175      2400                                     22 min. 625       408       130      1800                                     38 min. 1250      816       88       1200                                     40 min. 1875      1235      44       600                                      42 min. 2500      1625      0        0                                        ______________________________________                                    

As in the previous examples, the coatings were very uniform, and theiroptical characteristics were excellent.

Results of strain-to-microcracking (ε) tests obtained on samples 8 and 9are shown in Table 10 and compared with data obtained for controlsamples 10 and 11.

                  TABLE 10                                                        ______________________________________                                        Strain-To-Microcracking Results                                                                             Strain to                                       Sam- Thickness (μm)        micro-                                          ple  Pri-    VTMS     Gradational                                                                            SiO.sub.2                                                                            cracking ε                      No.  mer*    Sublayer Sublayer Sublayer                                                                             (in/in × 10.sup.2)                ______________________________________                                         8   --      0.05     1.0      2.5    0.45                                     9   5       0.05     1.0      2.5    0.47                                    10   --      --       --       2.0    0.33                                    11   5       --       --       2.0    0.35                                    ______________________________________                                        *Organosilicone                                                           

Higher ε values represent better strain-to-microcracking performance.Thus, it is readily apparent from this data that the gradational coatingoutperforms the other SiO₂ -containing structures, demonstrating that agradational coating indeed reduces the tensile stresses present at theinterface with the polycarbonate.

The desirable qualities achievable through a PECVD-applied gradationalcoating may also be confirmed by calculations of the mechanical stressesin such coatings as compared to a non-gradational coating. For example,ata given deposition temperature, the resulting stresses in the coatingand the substrate (after the structure had returned to room temperature)can be calculated by assuming known thermal expansion values and Young'smodulus values for each material.

Modifications and variations of the present invention are possible inlightof the above teachings. It should therefore be understood thatchanges may be made in the particular embodiments of the inventiondescribed which arewithin the full intended scope of the invention asdefined by the appended claims.

What is claimed is:
 1. An article comprising a plastic substrate and acoating disposed thereon, wherein said coating is characterized by agradual transition from a composition consisting essentially of aninterfacial material closest to the surface of the substrate to acomposition consisting essentially of an abrasion-resistant material onthe outer surface of said coating;said interfacial material beingselected from the group consisting of polymerization products oforganosilicon, organometallic, acrylic and olefin materials, and saidabrasion-resistant material being selected from the group consisting ofsilicon dioxide, silicon nitride, silicon oxynitride, silicon carbide,silicon carbonitride, boron oxide, boron nitride, aluminum oxide,aluminum nitride, titanium dioxide, tantalum oxide, iron oxide,germanium oxide, germanium carbide and mixtures thereof.
 2. The articleof claim 2 wherein the substrate is a polycarbonate material.
 3. Thearticle of claim 2 wherein a primer is disposed between thepolycarbonate and the interfacial material.
 4. The article of claim 2wherein the interfacial material is a polymerization product of anolefinic monomer.
 5. The article of claim 2 wherein the interfacialmaterial is a polymerization product of an acrylic monomer.
 6. Thearticle of claim 2 wherein the interfacial material is a polymerizationproduct of an organosilicon material.
 7. The article of claim 6 whereinthe organosilicon material is selected from the group consisting ofhexamethyldisilazane, hexamethyldisiloxane, vinyl trimethylsilane andoctamethylcyclotetrasiloxane.
 8. The article of claim 2 wherein theabrasion-resistant material is selected from the group consisting ofsilicon carbide, silicon dioxide, silicon nitride, silicon oxynitrideand mixtures thereof.
 9. The article of claim 8 wherein theabrasion-resistant material is silicon dioxide.